Product Description
Stock Display
Inspection and Packaging
1008 Cold Rolled Steel Coil
1008 cold rolled steel coil contains about 1.2% manganese and 0.4% silicon. There are also nickel, aluminium, chromium, copper and molybdenum present in small quantities in the carbon steels. AISI 1008 carbon steel coil has excellent weldability, which includes projection, butt, spot and fusion, and brazeability. 1008 cold rolled steel coil is mainly used in automobile, printed metal pail, building, building materials, and bicycle, etc. Besides, it is the best material to manufacture organic coated strip.
Product Parameters
| Product Name | 1008 Cold Rolled Steel Coil |
| Production Process | Hot Rolling, Cold Rolling |
| Material Standards | AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, etc. |
| Width | 100mm-3000mm |
| Length | 1m-12m, or Customized Size |
| Thickness | 0.1mm-400mm |
| Delivery Conditions | Rolling, Annealing, Quenching, Tempered or Standard |
| Surface Process | Ordinary, Wire Drawing, Laminated Film |
Chemical Composition
| Element | Content (%) |
|---|---|
| Iron, Fe | 99.31-99.7 % |
| Manganese, Mn | 0.30-0.50 % |
| Carbon, C | 0.10 % |
| Sulfur, S | 0.050 % |
| Phosphorous, P | 0.040 % |
Mechanical Properties
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 340 MPa | 49300 psi |
| Yield strength (depending on temper) | 285 MPa | 41300 psi |
| Elastic modulus | 190-210 Gpa | 27557-30458 ksi |
| Bulk modulus (typical for steel) | 200 GPa | 29000 ksi |
| Shear modulus (typical for steel) | 80.0 GPa | 11600 ksi |
| Poisson’s ratio | 0.27-0.30 | 0.27-0.30 |
| Elongation at break (in 50 mm) | 20 % | 20 % |
| Reduction of area | 45 % | 45 % |
| Hardness, Brinell | 95 | 95 |
| Hardness, Knoop (converted from Brinell hardness) | 113 | 113 |
| Hardness, Rockwell B (converted from Brinell hardness) | 55 | 55 |
| Hardness, Vickers (converted from Brinell hardness) | 98 | 98 |
| Machinability (based on AISI 1212 steel as 100 machinability)The machinability of group I bar, rod, and wire products can be improved by cold drawing) | 55 | 55 |
Scope of Application
AISI 1008 carbon steel is primarily used in extruded, cold headed, cold upset, and cold pressed parts and forms.ther large machinery that bears high loads.
FAQ
Related products
Galvanized C- Channel Steel
- OriginChina
- Delivery Time≥7 days
A36 carbon steel U channel provides excellent strength, weldability, and versatility, making it ideal for construction, fabrication, and structural support applications.
A105 Round Steel Bar
- OriginChina
- Delivery Time≥7 days
A105 round steel bar, offering excellent strength and toughness. Ideal for pressure vessels, flanges, and fittings in industrial applications requiring high performance and durability.
Global Automotive Steel Supplier
- OriginChina
- Delivery Time≥7 days
CJM offers a complete export-oriented range of automotive steel by application: chassis frame steel, structural AHSS, hot stamping steel, and EV battery platform steel. Serving Europe, India, South America, and more.