1008 Cold Rolled Steel Coil
1008 cold rolled steel coil contains about 1.2% manganese and 0.4% silicon. There are also nickel, aluminium, chromium, copper and molybdenum present in small quantities in the carbon steels. AISI 1008 carbon steel coil has excellent weldability, which includes projection, butt, spot and fusion, and brazeability. 1008 cold rolled steel coil is mainly used in automobile, printed metal pail, building, building materials, and bicycle, etc. Besides, it is the best material to manufacture organic coated strip.
Product Parameters
| Product Name | 1008 Cold Rolled Steel Coil |
| Production Process | Hot Rolling, Cold Rolling |
| Material Standards | AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, etc. |
| Width | 100mm-3000mm |
| Length | 1m-12m, or Customized Size |
| Thickness | 0.1mm-400mm |
| Delivery Conditions | Rolling, Annealing, Quenching, Tempered or Standard |
| Surface Process | Ordinary, Wire Drawing, Laminated Film |
Chemical Composition
| Element | Content (%) |
|---|---|
| Iron, Fe | 99.31-99.7 % |
| Manganese, Mn | 0.30-0.50 % |
| Carbon, C | 0.10 % |
| Sulfur, S | 0.050 % |
| Phosphorous, P | 0.040 % |
Mechanical Properties
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 340 MPa | 49300 psi |
| Yield strength (depending on temper) | 285 MPa | 41300 psi |
| Elastic modulus | 190-210 Gpa | 27557-30458 ksi |
| Bulk modulus (typical for steel) | 200 GPa | 29000 ksi |
| Shear modulus (typical for steel) | 80.0 GPa | 11600 ksi |
| Poisson’s ratio | 0.27-0.30 | 0.27-0.30 |
| Elongation at break (in 50 mm) | 20 % | 20 % |
| Reduction of area | 45 % | 45 % |
| Hardness, Brinell | 95 | 95 |
| Hardness, Knoop (converted from Brinell hardness) | 113 | 113 |
| Hardness, Rockwell B (converted from Brinell hardness) | 55 | 55 |
| Hardness, Vickers (converted from Brinell hardness) | 98 | 98 |
| Machinability (based on AISI 1212 steel as 100 machinability)The machinability of group I bar, rod, and wire products can be improved by cold drawing) | 55 | 55 |
Scope of Application
AISI 1008 carbon steel is primarily used in extruded, cold headed, cold upset, and cold pressed parts and forms.ther large machinery that bears high loads.
FAQ
Related products
BS4449 Steel Reinforcement Rebar
- OriginChina
- Delivery Time≥7 days
BS4449 steel reinforcement rebar, offering high strength and durability. Ideal for reinforced concrete structures in construction, infrastructure, and civil engineering projects.
1018 Cold Rolled Steel Coil
- OriginChina
- Delivery Time≥7 days
1018 cold rolled steel coil, known for its excellent strength, surface finish, and formability. Ideal for automotive, machinery, and manufacturing applications requiring high precision and durability.
Galvanized Unequal Angle Steel
- OriginChina
- Delivery Time≥7 days
Stainless Steel Angle Steel Stainless steel angle steel is a long strip of steel with two sides perpendicular to each other. There are equilateral stainless steel angle steel and unequal stainless steel angle steel. The two sides of the equilatera…
Stainless Steel H Steel
- OriginChina
- Delivery Time≥7 days
EN10034 Carbon Steel H Beam offers superior strength and durability, ideal for structural applications in construction and heavy machinery.