1018 Cold Rolled Steel Coil
1018 cold rolled steel coil is made of a general-purpose, low-carbon steel with good case hardening qualities. It is especially suited to cold forming and bending operations. 1018 steel is suitable for parts that require cold forming such as crimping, swaging, or bending. 1018 steel is mild steel with medium-low carbon content. AISI 1018 carbon steel is a free machining grade that is the most commonly available grade around the world. Although its mechanical properties are not very unique, it still can be easily formed, machined, welded and fabricated.
Product Parameters
| Product Name | 1018 Cold Rolled Steel Coil |
| Production Process | Hot Rolling, Cold Rolling |
| Material Standards | AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, etc. |
| Width | 100mm-3000mm |
| Length | 1m-12m, or Customized Size |
| Thickness | 0.1mm-400mm |
| Delivery Conditions | Rolling, Annealing, Quenching, Tempered or Standard |
| Surface Process | Ordinary, Wire Drawing, Laminated Film |
Chemical Composition
| Element | Content (%) |
|---|---|
| Manganese, Mn | 0.60-0.90 |
| Carbon, C | 0.15-0.20 |
| Sulfur, S | 0.05 (max) |
| Phosphorous, P | 0.04 (max) |
| Iron, Fe | Balance |
Mechanical Properties
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 440 MPa | 63800 psi |
| Yield strength | 370 MPa | 53700 psi |
| Modulus of elasticity | 205 GPa | 29700 ksi |
| Shear modulus (typical for steel) | 80 GPa | 11600 ksi |
| Poisson’s ratio | 0.29 | 0.29 |
| Elongation at break (in 50 mm) | 15 % | 15 % |
| Hardness, Brinell | 126 | 126 |
| Hardness, Knoop (converted from Brinell hardness) | 145 | 145 |
| Hardness, Rockwell B (converted from Brinell hardness) | 71 | 71 |
| Hardness, Vickers (converted from Brinell hardness) | 131 | 131 |
| Machinability (based on AISI 1212 steel. as 100 machinability) | 70 | 70 |
Scope of Application
AISI 1018 carbon steel is commonly used in high volume screw machine parts applications. The other applications of this alloy are as follows:
● Shafts
● Spindles
● Pins
● Rods
● Sprocket assemblies.g construction, used in cranes or other large machinery that bears high loads.
FAQ
Related products
Inconel 718 Bar
- OriginChina
- Delivery Time≥7 days
Inconel 718 Plate is a high-strength, heat-resistant alloy, ideal for high-temperature applications, offering excellent durability and corrosion resistance.
Stainless Steel H Steel
- OriginChina
- Delivery Time≥7 days
EN10034 Carbon Steel H Beam offers superior strength and durability, ideal for structural applications in construction and heavy machinery.
Titanium Grade 7 Plate
- MOQ 1 Ton
- OriginChina
Titanium Grade 7 Plate offers exceptional corrosion resistance, high strength, and excellent weldability, making it ideal for aggressive environments.
B500A/B500B/B500C Rebar
- OriginChina
- Delivery Time≥7 days
B500A rebar, offering high tensile strength and excellent durability. Ideal for reinforced concrete structures in construction and infrastructure projects.
loading…
已经是到最后一篇内容了！
MESSAGE：