Monel 500 Plate Description
Monel 500 is a high-strength nickel-copper alloy that contains approximately 65% nickel and 30% copper, along with small amounts of aluminum. This alloy is known for its excellent corrosion resistance and high mechanical strength, particularly in high-temperature environments. Monel 500 offers enhanced strength and oxidation resistance compared to Monel 400. It exhibits good resistance to corrosion in marine environments, high temperatures, and a variety of chemical exposures.
Product Parameters
| Product Name | Monel 500 Plate |
| Thickness | 0.3mm-200mm |
| Length | 2000mm, 2438mm, 3000mm, 5800mm, 6000mm, 12000mm, etc. |
| Width | 40mm-600mm, 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc. |
| Standard | ASTM, AISI, JIS, GB, DIN, EN, etc. |
| Surface | BA, 2B, NO.1, NO.4, 4K, HL, 8K, etc. |
| Certificate | ISO, SGS, BV |
| Production Technology | Hot Rolling, Cold Rolling |
Chemical Composition
| Nickel, minA | Copper | Al max | Manganese, max | Carbon, max | Silicon, max | Sulfur, max |
| 63.0-70.0% | 28.0% – 34.0% | 1.5-3.0% | 0.50% | 0.3% | 0.5% | 0.024% |
Mechanical Properties
| Condition (Temper) | Tensile Strength, min, psi (MPa) | Yield StrengthA(0.2 % offset), min, psi (MPa) | Elongationin 2 in. or50 mm, or4D, min,% | Rockwell Hardness(B Scale)b,c |
| Hot-Rolled Plate | ||||
| Annealed | 70000 (485) | 28000 (195) | 35 | – |
| As-RolledD,E | 75000 (515) | 40000 (275) | 25 | – |
| Hot-Rolled Sheet | ||||
| Annealed | 70000 (485) | 28000 (195) | 35 | – |
| Cold-Rolled Sheet | ||||
| Annealed | 70000 – 85000 (485 – 585) | 28000 (195) | 35 | – |
| Quarter-Hard | – | – | – | 73 – 83 |
| Half-Hard | – | – | – | 82 – 90 |
| Hard | 100000 (690) | 90000 (620) | 2 | – |
| Cold-Rolled Strip | ||||
| Annealed | 70000 – 85000 (485 – 585)F | 28000 (195) | 35F | – |
| Skin Hard | – | – | – | 68 – 73 |
| Quarter-Hard | – | – | – | 73 – 83 |
| Half-Hard | – | – | – | 82 – 90 |
| Three-Quarter-Hard | – | – | – | 89 – 94 |
| Hard | 100000 (690)F | 90000 (620)F | 2F | – |
| Spring Temper | – | – | – | 98 min |
Physical Performance
| Physical Performance | Units | Temperature in°C |
| Density | 8.80 g/cm³ | Room |
| Specific Heat | 0.385 Kcal/kg.C | 25° |
| Melting Range | 1300-1400°C | – |
| Modulus of Elasticity | 1.207 KN/mm² | 20° |
| Electrical Resistivity | 0.75 µΩ.cm | 20° |
| Coefficient of Expansion | 14.1 µm/m °C | 25 – 100° |
| Thermal Conductivity | 35 w/m-° K | 25° |
Scope of Application
Used in marine engineering, chemical and hydrocarbon processing equipment, gasoline tanks and fresh water tanks, crude oil distillers, degassing heaters, boiler feed water heaters and other heat exchangers, valves, pumps, shafts, accessories and fasteners, Industrial heat exchangers, chlorinated solvents, crude oil distillation columns, etc., chemical processing, pollution control, pulp and paper production; industrial and municipal waste treatment and acid natural gas recovery.
FAQ
Related products
High Strength Steel Plate for Construction
- OriginChina
- Delivery Time≥7 days
High-quality building construction steel plates for high-rise frames, large-span workshops, and warehouse projects. Fast delivery and global export experience.
Titanium Grade 2 Plate
- MOQ 1 Ton
- OriginChina
Titanium Grade 7 Plate offers exceptional corrosion resistance, high strength, and excellent weldability, making it ideal for aggressive environments.
Hastelloy X Pipe
- OriginChina
- Delivery Time≥7 days
Hastelloy C-22 Plate is a corrosion-resistant alloy, ideal for harsh environments, offering excellent resistance to pitting and stress corrosion.
Carbon Flat steel Steel Billets
- OriginChina
- Delivery Time≥7 days
Carbon flat steel billets offer excellent strength, durability, and machinability, ideal for manufacturing bars, sheets, and structural components.
loading…
已经是到最后一篇内容了！
MESSAGE：